A691 CM70 DOSBARTH21 TIWB
Pibell Dur Carbon ac Aloi A691, Wedi'i Weldio â Thrydan ar gyfer Gwasanaeth Pwysedd Uchel ar Dymheredd Uchel
Anfon ymchwiliad
Sgwrs Nawr
Cyflwyniad Cynnyrch
| TABL 1 Deunyddiau Plât | ||||
| Gradd Pibell | Math o Dur | Manyleb ASTM | HB, uchafswm A | |
| Rhif | Gradd | |||
| CM-65 | dur carbon-molybdenwm | A204/A204M | A | 201 |
| CM-70 | dur carbon-molybdenwm | A204/A204M | B | 201 |
| CM-75 | dur carbon-molybdenwm | A204/A204M | C | 201 |
| CMSH-70 | dur carbon-manganîs-silicon, wedi'i normaleiddio | A537/A537M | 1 | |
| CMS{{0% 7d% 7d | dur carbon-manganîs-silicon | A299/A299M | . . . | . . . |
| CMSH-80 | dur carbon-manganîs-silicon, wedi'i ddiffodd a'i dymheru | A537/A537M | 2 | |
| 1⁄2 CR | 1 ⁄ 2 % cromiwm, 1 ⁄ 2 % dur molybdenwm | A387/A387M | 2 | 201 |
| 1CR | 1 % cromiwm, 1 ⁄ 2 % dur molybdenwm | A387/A387M | 12 | 201 |
| 1 1 ⁄ 4 CR | 1 1 ⁄ 4 % cromiwm, 1 ⁄ 2 % dur molybdenwm | A387/A387M | 11 | 201 |
| 2 1 ⁄ 4 CR | 2 1 ⁄ 4 % cromiwm, 1 % dur molybdenwm | A387/A387M | 22 | 201 |
| 3CR | 3 % cromiwm, 1 % dur molybdenwm | A387/A387M | 21 | 201 |
| 5CR | 5 % cromiwm, 1 ⁄ 2 % dur molybdenwm | A387/A387M | 5 | 225 |
| 9CR | 9 % cromiwm, 1 % dur molybdenwm | A387/A387M | 9 | 241 |
| 91 | 9% cromiwm, 1% molybdenwm, fanadium, niobium C | A387/A387M | 91 B | 241 |
| TABL 2 Paramedrau Triniaeth Wres A | |||||
| Gradd Pibell | ASTM Manyleb |
Ôl-Weld Heat-Treat Amrediad Tymheredd (Lleihau Straen), gradd F ( gradd ) |
Normaleiddio Tymheredd, max oni bai nodir fel arall, gradd F ( gradd ) |
quenching Tymheredd, max oni bai nodir fel arall, gradd F ( gradd ) |
Tymheredd tymherus, 分钟, gradd F ( gradd ) |
| CM-65 | A204/A204M | 1100 至 1200 [590 至 650] | 1700 [925] | . . . | . . . |
| CM-70 | A204/A204M | 1100 至 1200 [590 至 650] | 1700 [925] | . . . | . . . |
| CM-75 | A204/A204M | 1100 至 1200 [590 至 650] | 1700 [925] | . . . | . . . |
| CMSH-70 | A537/A537M | 1100 至 1200 [590 至 650] | 1700 [925] | . . . | . . . |
| CMS{{0% 7d% 7d | A299/A299M | 1100 至 1200 [590 至 650] | 1700 [925] | . . . | . . . |
| CMSH-80 | A537/A537M | 1100 至 1200 [590 至 650] | 乙 | 1700 [925] | 1100 至 1250 [590 至 675] |
| 1⁄2 CR | A387/A387M | 1100 至 1300 [590 至 705] | 1850 [1010] | 1700 [925] | 1150 至 1375 [620 至 745] |
| 1CR | A387/A387M | 1100 至 1350 [590 至 730] | 1850 [1010] | 1700 [925] | 1150 至 1375 [620 至 745] |
| 11 % e2% 81% 84 4 CR | A387/A387M | 1100 至 1375 [590 至 745] | 1850 [1010] | 1700 [925] | 1150 至 1375 [620 至 745] |
| 21 ⁄ 4 CR | A387/A387M | 1200 至 1400 [650 至 760] | 1850 [1010] | 1700 [925] | 1250 至 1400 [675 至 760] |
| 3CR | A387/A387M | 1200 至 1400 [650 至 760] | 1850 [1010] | 1700 [925] | 1250 至 1400 [675 至 760] |
| 5CR | A387/A387M | 1200 至 1400 [650 至 760] | 1850 [1010] | 1650 [900] | 1300 至 1400 [705 至 760] |
| 9CR | A387/A387M | 1325 至 1375 [715 至 745] | C | . . . | 1325 至 1375 [715 至 745] |
| 91 | A387/A387M | 1350 至 1420 [730 至 770] | 1900 至 2000 [1040 至 1095] | 1900分钟[1040分钟] | 1350 至 1440 [730 至 780] |
| 类别名称如下 | |||
| 班级 | 管材热处理 | 射线照相, 参见章节 |
压力测试, 参见章节 |
| 10 | 没有任何 | 没有任何 | 没有任何 |
| 11 | 没有任何 | 9 | 没有任何 |
| 12 | 没有任何 | 9 | 8.3 |
| 13 | 没有任何 | 没有任何 | 8.3 |
| 20 | 应力消除,见5.3.1 | 没有任何 | 没有任何 |
| 21 | 应力消除,见5.3.1 | 9 | 没有任何 |
| 22 | 应力消除,见5.3.1 | 9 | 8.3 |
| 23 | 应力消除,见5.3.1 | 没有任何 | 8.3 |
| 30 | 归一化,见 5.3.2 | 没有任何 | 没有任何 |
| 31 | 归一化,见 5.3.2 | 9 | 没有任何 |
| 32 | 归一化,见 5.3.2 | 9 | 8.3 |
| 33 | 归一化,见 5.3.2 | 没有任何 | 8.3 |
| 40 | 正火和回火,见 5.3.3 | 没有任何 | 没有任何 |
| 41 | 正火和回火,见 5.3.3 | 9 | 没有任何 |
| 42 | 正火和回火,见 5.3.3 | 9 | 8.3 |
| 43 | 正火和回火,见 5.3.3 | 没有任何 | 8.3 |
| 50 | 淬火和回火,见5.3.4 | 没有任何 | 没有任何 |
| 51 | 淬火和回火,见5.3.4 | 9 | 没有任何 |
| 52 | 淬火和回火,见5.3.4 | 9 | 8.3 |
| 53 | 淬火和回火,见5.3.4 | 没有任何 | 8.3 |