### 1. Deunydd A213 T12
** sa213 t12 ** yn ** cromiwm-molybdenum dur aloi ** ar gyfer gwasanaeth tymheredd uchel . Mae wedi'i safoni o dan ASTM A213/A213M fel ** gradd T12 ** {.
---
### 2. SA213 Deunydd
**SA213 (ASTM A213/A213M)** is a specification for **seamless ferritic and austenitic alloy-steel boiler, superheater, and heat-exchanger tubes**. It covers grades like T2, T5, T9, T11, T12, T22, T91, TP304, ac ati ., a ddefnyddir mewn amgylcheddau pwysedd uchel/tymheredd .
---
### 3. Cyfansoddiad SA213 T9
** SA213 T9 ** Cyfansoddiad (ASTM A213/A213M):
- ** Carbon (C) **: 0.15% ar y mwyaf
- ** Manganîs (Mn) **: 0.30–0.60%
- ** ffosfforws (p) **: 0.025% ar y mwyaf
- ** Sylffwr (au) **: 0.025% ar y mwyaf
- ** Silicon (SI) **: 0.25–1.00%
- ** cromiwm (cr) **: 8.00–10.00%
- ** Molybdenwm (MO) **: 0.90–1.10%
*Dynodiad UNS: K90941*
---
### 4. SA 210 DEUNYDD
** SA210 (ASME SA210/ASTM A210) ** Gorchuddion ** Boeler dur canolig-carbon di-dor a thiwbiau uwch-wresogydd ** . Graddau allweddol:
- ** Gradd A1 **: Dur Carbon (Mn 0.27–0.93%)
- ** Gradd C **: Dur carbon cryfder uwch (Mn 0.29–1.06%)
*A ddefnyddir yn gyffredin mewn adrannau boeler tymheredd isel/canolig .*
---
### 5. Caledwch SA213 T91
** SA213 T91 ** Caledwch (ASTM A213/A213M):
- ** Ar ôl Normaleiddio a Thymheru **:
- ** Caledwch Uchaf **: 265 HBW (Brinell) neu 25 HRC (Rockwell C)
- ** Ystod nodweddiadol **: 190–250 HBW
*Mae caledwch rheoledig yn sicrhau cryfder ymgripiol a weldadwyedd ar gyfer gwasanaeth tymheredd uchel (hyd at 600 gradd) .*
Ar gyfer yr holl ddeunyddiau, cyfeiriwch at y manylebau ASTM/ASME diweddaraf ar gyfer profi a goddefiannau ardystiedig .